Steel Grade

AISI 4140/DIN 1.7225/JIS SCM440/GB 42CrMo

Size & Dimension

Dia:20-120mm L:2000-5800mm

Surface treatment

Black/Peeling/Polishing/Machined

Technique

Cold/Hot rolled, Cold-Drawn or Hot Forged

Heat Treatment

Annealed; Quenched; Tempered

Delivery Condition

Hot Rolled or Forged/Peeled or Black Surface/Annealed or QT

Test

SGS/UT100%/Elements Testing

Certificate

ISO/Mill Certificate

AVAILABLE Steel Type

Round bar/Plate

AVAILABLE SIZE:

Round bar: Diameter(mm) Max 800mm; Length(mm) Max 12000mm.

Plate: Thickness(mm) Max 800mm; Width(mm) Max 2300mm; Length(mm) Max 12000mm.

Condition: Cold rolled(drawn)≤50mm, Hot rolled≤12-250mm, Hot forged≥50mm.

 

AISI 4140/DIN 1.7225 Introduction:

AISI 4140 alloy steel is chromium, molybdenum, manganese containing low alloy steel. It has high fatigue strength, abrasion and impact resistance, toughness, and torsional strength.

 

Fabrication and Heat Treatment:

1. Forging

Preheat the steel carefully, then raise the temperature to 1150-1200°C for forging. Do not forge below 850°C.

2. Annealing

Heat the AISI 4140 slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 480°C followed by air cooling.

3. Stress Relieving

When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.

4. Hardening

AISI 4140 steel is usually supplied ready heat treated to 18-22HRC. If further heat treatment is required annealed AISI 4140 should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.

5. Tempering

Heat the AISI 4140 carefully to a suitable temperature selected by reference to a tempering chart or table (usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact value.

6. Surface Treatment

Plate: Origin Black, Orign cold rolled bright, Machined, Grinded

Bar: Origin Black, Orign cold rolled(drawn) bright, Turned, Peeled, Grinded

 

ABOUT US:

We specialize in 4140 and 4340 steels, which are versatile and have many advantages for a variety of industrial applications. Knowing the differences between them will help you choose the one that best suits your needs.

  â€‹Our advantages: Focus on the steel industry for more than ten years, strong factories, professional services, ensure quality, customize according to customer requirements, factory prices, fast transportation,Good after-sales service, pleasant cooperation, high repurchase rate and so on.

We offer a wide range of information and high quality steel products on 4140 and 4340 steel, for more information on our 4140 and 4340 steel products, please contact us today. To discuss pricing details, please request a quote.

 

CONTACT US:

MiKi Zhuo

E-mail:[email]

Skype/Whatsapp/Wechat:+86-18269260283

ADD:No.4 Dongda Street, Shatou, Changan Town, Dongguan City, Guangdong Province, P.R.C China

For more 4140 steel product information, please click this link:

Other Products